Experimental Research on the Performance of High-Temperature Bearing Steel Cr4Mo4 V

Author(s): Zenan Chu and Qiang He*

Volume 15, Issue 2, 2022

Published on: 25 May, 2021

Page: [195 - 205] Pages: 11

DOI: 10.2174/2212797614666210525115618

Price: $65

Abstract

Background: Cr4Mo4 V steel is widely used in high-temperature bearings because of its excellent high-temperature performance. Based on the research status of Cr4Mo4 V nationally and internationally, this paper explores its mechanical properties and friction properties at high temperatures.

Objective: To characterize the composition, microstructure, and properties of Cr4Mo4 V steel and explore its tensile properties, hardness, and friction properties at high temperatures.

Methods: Many methods are adopted, including chemical element analysis, metallographic analysis, hardness test, tensile test, damping test, and friction test.

Results: Cr4Mo4 V has a tempered martensite microstructure. The hardness and maximum tensile strength of Cr4Mo4 V decrease with increasing temperature. The grain of the Cr4Mo4 V steel after heating becomes refined, and the grain boundary increases. At room temperature, the surface friction coefficient and wear rate of Cr4Mo4 V steel decrease. Moreover, a Cr4Mo4 V steel-ceramic ball shows the best friction resistance. At high temperatures, the friction coefficient and wear of Cr4Mo4 V steel first decrease with increasing temperature and then increase sharply at 200°C.

Conclusion: With an increase in temperature, the hardness, breaking force, and tensile strength of Cr4Mo4 V bearing steel decrease, whereas the friction property increases. By analyzing the threedimensional morphology of different wear samples, the optimal working temperature of Cr4Mo4 V steel bearing is determined as 200°C.

Keywords: Cr4Mo4 V steel, high temperature, chemical composition, tensile stress, friction, damping test.

« Previous Next »
[1]
Zhang J. Application of ceramic materials on rolling bearings Bearing 1999; (2): 21-3.
[2]
Kun W, Feng H, Wen Z, Wu K-M. Research status and development trend of bearing steel. China Metallurgy 2020; 30(9): 119-28.
[3]
Voskamp AP. Material response to rolling contact loading. ASME. J Tribol 1985; 107(3): 359-66.
[http://dx.doi.org/10.1115/1.3261078]
[4]
Glaeser WA, Shaffer SJ. Contact Fatigue ASM Handbook, Fatigue and Fracture ASM International: Battelle Laboratories. 1996; 19: pp. 331-6.
[5]
Huo D, Xiao B. Curent situation and development prospect of bearing steel production. Sichuan Metallurgy 2015; 37(1): 63.
[6]
Parker RJ, Hodder RS. Rolling-element fatigue life of AMS 5749 corrosion resistant, high temperature bearing steel. Journal of Lubrication Technology 1978; 100(2): 226-32.
[http://dx.doi.org/10.1115/1.3453147]
[7]
Ruffing C, Ivanisenko Y, Kerscher E. A comparison of the fatigue and fracture behavior of high strength ultrafine grained medium carbon steel SAE 1045 with high strength bearing steel SAE 52100. Procedia Structural Integrity 2016; 2: 3240-7.
[http://dx.doi.org/10.1016/j.prostr.2016.06.404]
[8]
Srinivasa N, Prasad YVRK. Hot working characteristics of nimonic 75, 80A and 90 superalloys: A comparison using processing maps. J Mater Process Technol 1995; 51(1-4): 171-92.
[http://dx.doi.org/10.1016/0924-0136(94)01602-W]
[9]
Medeiros SC, Prasad YVRK, Frazier WG, et al. Modeling grain size during hot deformation of IN 718. Scr Mater 1999; 42(1): 17-23.
[http://dx.doi.org/10.1016/S1359-6462(99)00316-4]
[10]
Prasad YVRK, Rao KP. Processing maps and rate controlling mechanisms of hot deformation of electrolytic tough pitch copper in the temperature range 300–950°C. Mater Sci Eng A 2005; 391(1-2): 141-50.
[http://dx.doi.org/10.1016/j.msea.2004.08.049]
[11]
Fan Chonghui. The development of technology of steels used for bearings in China Development and application of materials 1999; 14(5): 41-6.
[12]
Fang F, Li H, et al. Grinding experiment of Cr4Mo4V high temperature bearings steel Bearing 2005; 6: 24-5.
[13]
Jin J, Chen Y, Gao K, et al. The effect of ion implantation on tribology and hot rolling contact fatigue of Cr4Mo4Ni4V bearing steel. Appl Surf Sci 2014; 305: 93-100.
[http://dx.doi.org/10.1016/j.apsusc.2014.02.174]
[14]
Gong J, Lei J. Effect of heat treatment process on microstructures and fracture toughness of steel Cr4Mo4V. Bearing 2015; 9: 35-7.
[15]
Murty SVSN, Rao BN. On the development of instability criteria during hotworking with reference to IN 718. Mater Sci Eng A 1998; 254(1-2): 76-82.
[http://dx.doi.org/10.1016/S0921-5093(98)00764-3]
[16]
Murty SVSN, Rao BN. On the flow localization concepts in the processing maps of IN718. Mater Sci Eng A 1999; 267(1): 159-61.
[http://dx.doi.org/10.1016/S0921-5093(99)00122-7]
[17]
Narayana Murty SVS, Nageswara Rao B, Kashyap BP. Instability criteria for hot deformation of materials. Int Mater Rev 2000; 45(1): 15-26.
[http://dx.doi.org/10.1179/095066000771048782]
[18]
Murty SVSN, Rao BN, Kashyap BP. Development and validation of a processing map for zirconium alloys. Model Simul Mater Sci Eng 2002; 10(5): 503-20.
[http://dx.doi.org/10.1088/0965-0393/10/5/303]
[19]
Prasad YVRK. Recent advances in the science of mechanical processing. Indian J Technol 1990; 28: 435-51.
[20]
Espejel GEM, Gabelli A. A Model for rolling bearing life with surface and subsurface survival: Sporadic surface damage from deterministic indentations. Tribol Int 2016; 96: 279-88.
[http://dx.doi.org/10.1016/j.triboint.2015.12.036]
[21]
Bhattacharyya A, Subhash G, Arakere N, et al. Influence of residual stress and temperature on the cyclic hardening response of M50 high-strength bearing steel subjected to rolling contact fatigue. J Eng Mater Technol 2016; 138(2)021003
[22]
Evans MH. White Structure Flaking (WSF) in wind turbine gearbox bearings: Effects of ‘butterflies’ and White Etching Cracks (WECs). Mater Sci Technol 2012; 28(2): 3-22.
[http://dx.doi.org/10.1179/026708311X13135950699254]
[23]
Guetard G, Toda-Caraballo I, Rivera-Diaz-Del-Castillo PEJ. Damage evolution around primary carbides under rolling contact fatigue in VIM-VAR M50. Int J Fatigue 2016; 91(PT.1): 59-67.
[http://dx.doi.org/10.1016/j.ijfatigue.2016.05.026]
[24]
Zhong-Yu P, Bin-Shi X, Hai-Dou W, et al. Investigation of rolling contact fatigue lives of Fe-Cr alloy coatings under different loading conditions. Surf Coat Tech 2010; 204(9): 1405-11.
[http://dx.doi.org/10.1016/j.surfcoat.2009.09.035]
[25]
Tang GZ. Cr4Mo4V steel high-temperature shot blasting method. CN201710814409.0 (2017). 2017.
[26]
Tang GZ, Ma XX, Wang LQ, et al. Cr4Mo4V steel bearing powerful shot blasting and heating injection/permeation composite surface strengthening method. CN201510547238.0 (2015).
[27]
Tang GZ, Ma XX, Li ZW. Cr4Mo4V steel bearing carbonnitrogen plasma radical ion carburizing method by means of warming. CN201110051321.0 (2011).
[28]
Xu FJ, Ma XX, Tang GZ. Molybdenum-containing bearing steel surface strengthening process. CN201310074930.7 (2013).
[29]
Shen W, Li Z, Li G, et al. Thermal treatment method for dimensional stability of Cr4Mo4V steel bearing ring. CN201410555822.6 (2014).
[30]
Xia YZ, Yu X, Ma X, et al. Dimensional stability treatment technique for 8Cr4Mo4V bearing part. CN201710516172.8 (2017).
[31]
Ma X, Tang G. Thermal-cold cycling treatment process for increasing size stability of high-temperature bearing steel parts. CN201810031553.1 (2018).
[32]
Deng J. Heat treatment process of high-temperature resistant roller bearing steel. CN201710523423.5 (2017).
[33]
Yu X, Wei Y, Sun J, et al. A heat treatment method for controlling the dimension variation of high temperature bearing steel. CN202010108534.1 (2020).
[34]
Zhao Kaili, Wu Tingbao. Yu Xingfu et al. Isothermal quenching heat treatment method for improving toughness of 8Cr4Mo4V steel. CN201711001849.0 (2017).
[35]
Gong Jianxun, Chen Huizhen, Song Huahua. Air quenching process for high-temperature bearing steel ferrule. CN201410537993.6 (2014).
[36]
Li Fuwei, You Shaojun, Song Huahua, et al. Shaping machining method of bearing ring prepared from high-temperature bearing steel. CN201810165943.8 (2018).
[37]
Luo Haiwen, Ping Yang. Preparation method of bearing steel capable of resisting high temperature of 400 DEG C. CN201710194788.8 (2017)
[38]
Xu Kaibin. ,Liu Xianmin,Xia Suping et al. High-temperatureresistant bearing steel and production process thereof. CN201210480807.0 (2012).
[39]
Gu XG, Shen SD, Hu HX, et al. Rolling cogging production method of Cr4Mo4V electroslag steel ingot. CN200410053946.0 (2004)
[40]
Li RR. High-temperature resistant bearing steel. CN201410698509.8 (2014).
[41]
Zheng XP. Abrasion resistant and high-temperature resistant bearing steel. CN201610984602.4 (2016)
[42]
Rachkov VI, Obraztsov SM. Analysis and prediction of the physico-mechanical properties of reactor steel by means of artificial intelligence and applied statistics. At Energy 2014; 116(5): 311-4.
[43]
Shun G, Yu J, Liu X, et al. A predicting model for properties of steel using the industrial big data based on machine learning. Comput Mater Sci 2019; 160: 95-104.
[http://dx.doi.org/10.1016/j.commatsci.2018.12.056]
[44]
Deriving temperature-dependent material models for structural steel through artificial intelligence. Constr Build Mater 2018; 191: 56-68.
[http://dx.doi.org/10.1016/j.conbuildmat.2018.09.186]
[45]
Tang G, Ren L, Ma X, et al. Construction of Cr4Mo4V bearing steel hot working drawing. Defense Manufacturing Technology 2015; 03: 37-42.
[46]
Guo J, Yang M, Lu D, Li X. Rolling contact fatigue and wear characteristics of Cr4Mo4V bearing steel. Tribology 2017; 37(2): 155-66.
[47]
Guo J, Yang M, Lu D, Li X. Rotational bending fatigue life and fatigue crack initiation mechanism of Cr4Mo4V bearing steel. Journal of Materials Engineering 2019; 47(7): 134-43.

Rights & Permissions Print Cite
Article Metrics
22
1
© 2024 Bentham Science Publishers | Privacy Policy