Advances in Carbidic Austempered Ductile Iron (CADI) - A Wearresistant Material

Author(s): Lakshmiprasad Maddi*, Ajay Likhite

Journal Name: Current Materials Science
Formerly Recent Patents on Materials Science

Volume 14 , Issue 2 , 2021


Become EABM
Become Reviewer
Call for Editor

Graphical Abstract:


Abstract:

Background: Ductile irons provide a more viable alternative for malleable cast iron in areas that do not demand extreme wear resistance. Austempering of ductile irons was a well researched area in the last two decades. Attempts to further improve the wear resistance led to the development of Carbidic austempered ductile iron (CADI), wherein the carbides contribute to wear resistance. Combination of ausferritic matrix, graphite nodules, and carbides (eutectic and alloy) symbolizes the microstructure of CADI.

Methods: Two principal approaches adopted by the researchers to change the microstructure are (i) addition of carbide forming elements (ii) heat treatment (s).

Results: Both the above methods result in the refinement of graphite nodules, carbide precipitations, along fine ausferrite.

Conclusion: Improvement in hardness, toughness and wear resistance was observed largely as a consequence of fine carbide precipitations and formation of martensite.

Keywords: Ductile iron, alloy carbides, austempering, tribology, ausferrite, two step austempering.

Rights & PermissionsPrintExport Cite as

Article Details

VOLUME: 14
ISSUE: 2
Year: 2021
Published on: 23 April, 2021
Page: [114 - 124]
Pages: 11
DOI: 10.2174/2666145414666210423125555
Price: $65

Article Metrics

PDF: 264