Mechanical Performance of the Phosphogypsum Baking-free Bricks

Author(s): Xiaoyu Guo, Yajing Mao, Lizhai Pei*, Chuangang Fan

Journal Name: Current Materials Science
Formerly Recent Patents on Materials Science

Volume 14 , Issue 2 , 2021

Become EABM
Become Reviewer
Call for Editor

Graphical Abstract:


Background: A large amount of phosphogypsum occupies the land and causes environmental pollution. It is of great research significance and urgency to the utilization of the phosphogypsum.

Methods: The influence of the ratio of the cementing materials and phosphogypsum (C/P ratio) on the compressive strength, water absorption, softening coefficient and freeze-thaw stability of the phosphogypsum baking-free bricks was investigated. The consolidation process of the phosphogypsum baking-free bricks was analyzed by X-ray diffraction (XRD) and scanning electron microscopy (SEM).

Results: XRD patterns show that the phosphogypsum baking-free bricks curved for 28 d are mainly composed of monoclinic CaSO4·2H2Oand hexagonal Ca6Al2(SO4)3(OH)12·26H2O (Aft) phases. SEM observation shows that the phosphogypsum bricks consist of Aft nanorods and irregular microscale particles. The softening coefficient, water-resistant performance and freezethaw stability of the phosphogypsum baking-free bricks remarkably decrease with decreasing the C/P ratio. 28 d compressive strength decreases from 26.42 MPa to 15.58 MPa with the change of the C/P ratio from 1:1 to 1:2.5. The optimal ratio of the cementing materials and phosphogymsum is 1:1. The phosphogypsum baking-free bricks exhibit good stability after 18 freeze-thaw cycles.

Conclusion: Phosphogypsum baking-free bricks were prepared by natural curing process using phosphogypsum as the raw materials, cement, slag, fly ash and silica fume as the cementing materials. The phosphogypsum baking-free bricks exhibit great application in the field of building materials.

Keywords: Phosphogypsum, baking-free bricks, mechanical performance, X-ray diffraction, scanning electron microscopy, cementing materials.

Rights & PermissionsPrintExport Cite as

Article Details

Year: 2021
Published on: 02 February, 2021
Page: [131 - 140]
Pages: 10
DOI: 10.2174/2666145414666210203115332
Price: $65

Article Metrics

PDF: 437