Steel Corrosion and Control in Concrete Made with Seawater

Author(s): Arpit Goyal*, S.R. Karade

Journal Name: Innovations in Corrosion and Materials Science
Formerly Recent Patents on Corrosion Science

Volume 10 , Issue 1 , 2020

Become EABM
Become Reviewer

Graphical Abstract:


Abstract:

Background: Water scarcity is amongst the biggest problems the world is facing in the 21st century. To reduce the consumption of Potable Water (PW) in construction industries and to make concrete construction more sustainable, its replacement with Seawater (SW) has been explored. Technical literature on this subject is not widely available. Such investigations are necessary for determining suitable remedial measures for the effective utilization of seawater for making sustainable concrete.

Objective: In the present study, use of Seawater (SW) has been explored as both mixing and curing water in concrete. To counter the adverse effects of seawater on strength and corrosion resistance, use of Fly Ash (FA) and Red Mud (RM) as cement replacements in the seawater concrete had been investigated.

Methods: The possibility of the use of seawater in making concrete has been explored by literature and experimental investigations. The obtained results are discussed in light of the information available in the literature. Various tests were performed such as compressive strength, Half-cell potential, electrochemical impedance spectroscopy and microstructural analysis using SEM and XRD.

Results: Results showed higher compressive strength and improved corrosion resistance for Seawater Concrete (SWC) with FA & RM as compared to Potable Water Concrete (PWC) specimens. SWC specimens without supplementary cementitious materials show lower electrical resistivity and potential more negative than -450 mV indicating severe corrosion. 30% FA and 5% RM is identified as the optimum combination for the most favorable response in terms of mechanical strength and electrical resistivity of seawater concrete. After 90 days, the compressive strength of 35.77 MPa was achieved.

Conclusion: Combination of both FA and RM in SWC reduces chloride migration and increases chloride binding by the formation of Friedel’s salt. Half-cell potential (HCP) and Electrochemical Impedance Spectroscopy (EIS) results confirmed a reduction in corrosion rate in SWC specimens with fly ash and red mud.

Keywords: Corrosion, seawater, fly ash, red mud, reinforced concrete, electrochemical impedance spectroscopy (EIS).