Strong Quantum Confinement Effects in Nanometer Devices with Graphene Directly Grown on Insulator by Catalyst-free Chemical Vapor Deposition

Author(s): Hiroto Sato, Atsushi Nakamura, Amit Banerjee, Kenji Yamada, Hiroaki Satoh, Jiro Temmyo, Hiroshi Inokawa*

Journal Name: Current Graphene Science (Discontinued)

Volume 1 , Issue 1 , 2017

Graphical Abstract:


Background: The understanding of electrical properties of defective graphene in nanometer regime has lagged behind. Objective: This report intends to characterize defective but practically useful graphene as nanometer devices.

Method: A-few-layer-thick graphene was directly grown on SiO2 substrate by alcohol-chemical vapor deposition (alcohol-CVD) using ethanol as carbon source and without the use of any catalytic metal. The graphene film was delineated into nanometer structures by electron beam lithography to make the nanoscale devices.

Results: The Raman spectra of the graphene sheet on SiO2 shows relatively large D peak, which means the graphene is defective and consists of nanograins with an estimated size of 17 nm. Modulation of the graphene resistance by the gate voltage Vg was studied at room temperature. The film shows only p-type conduction, with a sheet resistance of 3.7 kΩ / and field-effect mobility calculated to be 44 cm2/Vs. From the temperature dependence of the graphene sheet, it is found that the resistance increases only by 7% from room temperature to 10 K, indicating low potential barrier between the domains, even though the graphene film is as thin as 1.6 nm and defective. From the conductance (Id/Vd) contour plot measured at 10 K of these nanodevices, aperiodic Coulomb-blockade feature and transport with a large gap were observed.

Conclusion: Correlation among narrowest constriction widths, the variation of the addition energies and transport gaps in disordered graphene nanostructures is evident. These graphene nanodevices may have promising application in various nanodevices like single-electron (or single-hole) transistor, singlemolecule transistor, van-der-Waals stacked nanodevices, etc.

Keywords: Graphene nanostructures, Coulomb blockade, graphene nanometer devices, alcohol chemical vapor deposition, electron beam lithography, Raman spectra, sheet resistance.

promotion: free to download

Rights & PermissionsPrintExport Cite as

Article Details

Year: 2017
Published on: 16 July, 2017
Page: [44 - 48]
Pages: 5
DOI: 10.2174/2452273201666170221124819

Article Metrics

PDF: 37