Preparation of the Al-CNT (Carbon Nanotubes) Compound Material by High Energy Milling

Author(s): Cai Xiaolan, Wang Xiaofei.

Abstract:

This paper using high energy ball milling (HEM), researched has discussed the preparation of Al-CNT compound materials at the different milling times, rotary speeds, amount of CNT and sinter technology for their properties of hardness and density and for the preparation the Al-CNT. The milling time is about 30 to 100 min, with a rotational speed of about 300-600/rpm and the wt% of CNT being 0-5%. This paper has analyzed the XRD patterns. SEM and STM micrograph, and the results showed that the Al material could be reinforced by CNT using HEM. The hardness of Al-CNT is 75 HB with a density of 2.65 g/cm3 when milling is carried out for 90 min, at CNT being 3%.

Keywords: High energy milling(HEM), Al-CNT, compound material, rotary speeds, Carbon Nanotubes

Order Reprints Order Eprints Rights & PermissionsPrintExport

Article Details

VOLUME: 8
ISSUE: 1
Year: 2012
Page: [33 - 37]
Pages: 5
DOI: 10.2174/1573413711208010033