A Comparison of Different Methods of MWCNTs Metalation in a Single Step Using Three Different Silver-containing Compounds

Author(s): Beatriz O. García, Oxana V. Kharissova, Rasika Dias, Francisco S. Aguirre-Tostado, César Leyva, Lucy T. González, Boris I. Kharisov*.

Journal Name: Recent Patents on Nanotechnology

Volume 13 , Issue 1 , 2019

Become EABM
Become Reviewer

Graphical Abstract:


Abstract:

Background: Synthesis and applications of Ag-coated carbon nanotubes are currently under intensive research, resulting in a series of recent patents. Silver nanoparticles are normally obtained from silver nitrate. However, there are also other silver-containing compounds that can facilitate the production of silver nanoparticles, such as silver(I) acetate and silver(II) oxide. Being combined with carbon nanotubes, silver nanoparticles can transfer to them some of their useful properties, such as conductivity and antibacterial properties, and contribute to improving their dispersion in solvents.

Objective: To apply three different silver-containing precursors of Ag nanoparticles for the decoration of carbon nanotubes and study the morphology of formed composites by several methods.

Method: Three different silver compounds were used as Ag source to carry out the functionalization and decoration of carbon nanotubes under ultrasonic treatment of the reaction system, containing, commercial carbon nanotubes, organic peroxides as oxidants or hydrazine as a reductant, and a surfactant. Resulting samples were analyzed by XRD and XPS spectroscopy, as well as TEM and SEM microscopy to study the morphology of formed nanocomposites.

Results: Silver nanoparticles can be produced without the presence of a reducing agent. Applying hydrazine, as a reducing agent, it is possible to obtain functionalized carbon nanotubes doped with silver nanoparticles, in which their sizes are smaller (1-5 nm) compared to those obtained without using hydrazine.

Conclusion: Silver nanoparticles having a size range between 2-60 nm can be produced without the presence of a reducing agent. The use of a reducing agent, such as hydrazine, affects the size of silver nanoparticles.

Keywords: Carbon nanotubes, silver, decoration, hydrazine, TEM, SEM.

[1]
Gupta VK, Saleh TA. Column with CNT/magnesium oxide composite for lead(II) removal from water. Environ Sci Pollut Res Int 2012; 19(4): 1224-8.
[2]
Kumar NA, Kim SH, Cho BG, Lim KT, Jeong YT. Surface functionalization of multiwalled carbon nanotubes with poly(3,4-propylenedioxythiophene) and preparation of its random copolymers: New hybrid materials. Colloid Polym Sci 2009; 287: 97-102.
[3]
Sahoo NG, Bao H, Pan Y, et al. Functionalized carbon nanomaterials as nanocarriers for loading and delivery of a poorly water-soluble anticancer drug: A comparative study. Chem Commun 2011; 47: 5235-7.
[4]
Sepahavand R, Adeli M, Astinchap B, Kabiri R. New nanocomposites containing metal nanoparticles, carbonnanotube and polymer. J Nanopart Res 2008; 10: 1309-18.
[5]
Le TV, Ngo CL, Le QT, Ngo TT, Nguyen DN, Vu MT. Surface modification and functionalization of carbon nanotube with some organic compounds. Adv Nat Sci Nanosci Nanotechnol 2013; 4: 1-5.
[6]
Edwards ER, Antunes EF, Botelho EC, Baldan MR, Corat EJ. Evaluation of residual iron in carbon nanotubes purified by acid treatments. Appl Surf Sci 2011; 258: 641-8.
[7]
Cruz-Delgado VJ, Ávila-Orta CA, Pérez-Camacho O, García-Zamora M, Comparán-Padilla VE, Medellín-Rodríguez FJ. Funcionalización de nanotubos de carbono para la preparación de nanocompuestos poliméricos. Ideas CONCYTEG 2011; 6(72): 675-92.
[8]
Chen W, Lu H, Nutt SR. The influence of functionalized MWCNT reinforcement on the thermomechanical properties and morphology of epoxy nanocomposites. Compos Sci Technol 2008; 68: 2535-42.
[9]
Porro S, Musso S, Vinante M, et al. Purification of carbon nanotubes grown by thermal CVD. Physica E 2007; 37: 58-61.
[10]
Carson L, Kelly-Brown C, Stewart M, et al. Synthesis and characterization of chitosan-carbon nanotube composites. Mater Lett 2009; 63: 617-20.
[11]
Roh SC, Choi EY, Choi YS, Kim CK. Characterization of the surface energies of functionalized multi-walled carbon nanotubes and their interfacial adhesion energies with various polymers. Polymer 2014; 55: 1527-36.
[12]
Wang J, Chen Y, Li R, et al. Graphene and carbon nanotube polymer composites for laser protection. J Inorg Organomet Polym 2011; 21: 736-46.
[13]
Hong BH, Bae SC, Lee CW, Jeong S, Kim KS. Ultrathin single-crystalline silver nanowire arrays formed in an ambient solution phase. Science 2001; 294: 348-51.
[14]
Yang R, Sui CH, Gong J, Qu LY. Single-crystal silver nanowires: Preparation and surface-enhanced Raman scattering (SERS) property. Mater Lett 2007; 61: 900.
[15]
Barbic M, Mock JJ, Smith DR, Schultz S. Single crystal silver nanowires prepared by the metal amplification method. J Appl Phys 2002; 91: 9341.
[16]
Choi JS, Sauer GD, Nielsch K, Wehrspohn RB, Gsele U. Hexagonally arranged monodisperse silver nanowires with adjustable diameter and high aspect ratio. Chem Mater 2003; 15: 776.
[17]
Chen J. Preparation method of silver composite antibacterial material of carbon nanotube. CN103843822A, 2014
[18]
Douglas J. Coatings comprising carbon nanotubes atent US20080044651A1, 2005.
[19]
Kim YJ, Ko CM, Cho HS. Conductive paste containing silver-decorated carbon nanotubesPatent US20110247866A1, 2011
[20]
Chao F, Huafeng JW, Mo Z. Polyaniline/carbon nano tube/ nanometer silver particle conductive composite material and preparation method thereof. Patent CN101525435A, 2009
[21]
Shen C, Yang M, Chen K. The method of producing a highly conductive carbon nanotube-based conductive coating Patent CN108485356A, 2018
[22]
Kim YJ, Ko CM, Cho HS. Conductive paste containing silverdecorated carbon nanotubes. US20110247866A1, 2008.
[23]
Yu J, Huang T, Jiang Z, Qi L, Jiang R. Species BN/CuAg/CNT composite material and its preparation and use. Patent CN108306023A, 2018
[24]
Fang D, Bao R, Yi J, Li X. . Metal coated carbon nanotube reinforced preparing metal matrix composite. CN108441662A, 2018
[25]
Leu C, Yu TC, Chen GL. Thermal interface with silver-filled carbon nanotubesPatent US7148512B2, 2004
[26]
Coulombe S, Meunier JL, Hordy N, Jorge L, Vandsburger L, Roche P. Nanofluid with nanoparticle-decorated multiwall carbon nanotubes and method of preparation thereof. US20160045882A1, 2013
[27]
Li YA, Tai NH. Method for decoration of silver onto carbon materials. US9023250B2, 2013
[28]
Ramaprabhu S, Baro M, Nayak P, Theres Baby T. Metal nanoparticle decorated carbon nanotubes and methods of preparation and use. US20140377790A1, 2013
[29]
Kim, Jang-jae, Feng, Changmoo-chan, Chin-hwan. Method of fabricating silver nanoparticle decorated carbon nanotube nanocomposites. KR20090117195A, 2008
[30]
Kim SH, Choi WI, Kim KH, Yang DJ, Heo S, Yun DJ. Nanoscalechemical and electrical stabilities of graphene-covered silver nanowire networks for transparent conducting electrodes. Sci Rep 2016; 6: 33074.
[31]
Dwivedi, Neeraj & Yeo, Reuben & Satyanarayana, Nalam & Kundu, Shreya & Tripathy, Sudhiranjan & S Bhatia, C. (2015)
[32]
Frueh J, Nakashima N, He Q, Möhwald H. Effect of linear elongation on carbon nanotube and polyelectrolyte structures in PDMS-supported nanocomposite LbL Films. J Phys Chem B 2012; 116(40): 12257-62.
[33]
Datsyuk V, Kalyva M, Papagelis K, et al. Chemical oxidation of multiwalled carbon nanotubes. Carbon 2008; 46: 833-40.
[34]
Li W, Gai M, Frueh J, Kudryavtseva VL, Sukhorukov GB. Polyelectrolyte multilayer microchamber-arrays for in situ cargo release: Low frequency vs. medical frequency range ultrasound. Colloids Surfaces A Physicochem Eng Asp 2018; 547: 19-27


Rights & PermissionsPrintExport Cite as

Article Details

VOLUME: 13
ISSUE: 1
Year: 2019
Page: [59 - 69]
Pages: 11
DOI: 10.2174/1872210513666190225095537
Price: $58

Article Metrics

PDF: 56
HTML: 11