Effects of Calcination on Sol-gel Synthesis of Hollow Spherical 8%B-TiO2 for Photocatalytic Degradation of RBR X-3B -Characterization and Activity

Author(s): Lili Yang, Yao Zhao, Jing Li, Yanwen Zhou, Xuan Xiao, Wenjie Zhang*.

Journal Name: Current Nanoscience

Volume 15 , Issue 3 , 2019

Become EABM
Become Reviewer

Graphical Abstract:


Abstract:

Background: TiO2-based materials can be utilized in both polluted air and wastewater treatments. Ion doping is the most applied modification method, and many kinds of metal ions and nonmetal ions are doped into a TiO2 crystalline skeleton. The hollow spherical photocatalyst can both easily suspend in wastewater under aeration and settle down after treatment to release the water.

Methods: The hollow spherical B-TiO2 photocatalyst was prepared by a sol-gel method. Tetrabutyl titanate and tributyl borate were used as the titanium and boron sources. The materials were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), infrared spectrum (FTIR), and N2 adsorption-desorption techniques.

Results: The 8%B-TiO2 material is composed of anatase TiO2 when the calcination temperature is below 600°C. The graphical template is burnt out during calcination to leave a hole in the spherical 8%B-TiO2. The BET surface area of the materials declines from 53.2 m2/g at 400°C to 10.6 m2/g at 700°C. High-temperature thermal treatment results in the small surface area and large pore size. The activity of the 8%B-TiO2 materials was studied on adsorption and photocatalytic degradation of RBR X-3B dye. The 8%B-TiO2 sample prepared at 600°C has the maximum activity on RBR X-3B degradation. After five cycles, decoloration efficiency on the 8%B-TiO2 decreases from 100% in the first cycle to 80% in the fifth cycle.

Conclusion: Photocatalytic activity of the hollow spherical material depends on calcination temperature with the optimum activity on the sample obtained at 600°C. The hollow spherical 8%B-TiO2 has satisfactory performance for recycling. Photocatalytic degradation of RBR X-3B can be proven by the UV-Vis spectra during the degradation process.

Keywords: Photocatalytic degradation, calcination, boron-doped, TiO2, hollow spherical, sol-gel.

[1]
Nezamzadeh-Ejhieh, A.; Banan, Z. Sunlight assisted photodecolorization of crystal violet catalyzed by CdS nanoparticles embedded on zeolite A. Desalination, 2012, 284(4), 157-166.
[2]
Nezamzadeh-Ejhieh, A.; Karimi-Shamsabadi, M. Decolorization of a binary azo dyes mixture using CuO incorporated nanozeolite-X as a heterogeneous catalyst and solar irradiation. Chem. Eng. J., 2013, 228, 631-641.
[3]
Derikvandi, H.; Nezamzadeh-Ejhieh, A. Comprehensive study on enhanced photocatalytic activity of heterojunction ZnS-NiS/zeolite nanoparticles: Experimental design based on response surface methodology (RSM), impedance spectroscopy and GC-MASS studies. J. Colloid Interface Sci., 2017, 490, 652-664.
[4]
Zhang, W.J.; Ma, Z.; Du, L.; Yang, L.L.; Chen, X.J.; He, H.B. Effects of calcination temperature on characterization and photocatalytic activity of La2Ti2O7 supported on HZSM-5 zeolite. J. Alloys Compd., 2017, 695, 3541-3546.
[5]
Zhang, W.J.; Bi, F.F.; Yu, Y.; He, H.B. Phosphoric acid treating of ZSM-5 zeolite for the enhanced photocatalytic activity of TiO2/HZSM-5. J. Mol. Catal.A Chem., 2013, 372, 6-12.
[6]
Zhou, P.; Wu, J.H.; Yu, W.L.; Zhao, G.H.; Fang, G.J.; Cao, S.W. Vectorial doping-promoting charge transfer in anatase TiO2 0 0 1 surface. Appl. Surf. Sci., 2014, 319, 167-172.
[7]
Ku, Y.; Shiu, S.J.; Wu, H.C. Decomposition of dimethyl phthalate in aqueous solution by UV–LED/TiO2 process under periodic illumination. J. Photochem. Photobiol.A Chem., 2017, 332, 299-305.
[8]
Zhang, W.J.; Wang, K.L.; Yu, Y.; He, H.B. TiO2/HZSM-5 nano-composite photocatalyst: HCl treatment of NaZSM-5 promotes photocatalytic degradation of methyl orange. Chem. Eng. J., 2010, 163, 62-67.
[9]
Babaahamdi-Milani, M.; Nezamzadeh-Ejhieh, A. A comprehensive study on photocatalytic activity of supported Ni/Pb sulfide and oxide systems onto natural zeolite nanoparticles. J. Hazard. Mater., 2016, 318, 291-301.
[10]
Zhang, W.J.; Liu, Y.X.; Pei, X.B.; Chen, X.J. Effects of indium doping on properties of xIn-0.1%Gd-TiO2 photocatalyst synthesized by sol-gel method. J. Phys. Chem. Solids, 2017, 104, 45-51.
[11]
Du, J.; Li, X.Y.; Li, K.; Gu, X.; Qi, W.Q.; Zhang, K. High hydrophilic Si-doped TiO2 nanowires by chemical vapor deposition. J. Alloys Compd., 2016, 687, 893-897.
[12]
Juma, A.; Acik, I.O.; Oluwabi, A.T.; Mere, A.; Mikli, V.; Danilson, M.; Krunks, M. Zirconium doped TiO2 thin films deposited by chemical spray pyrolysis. Appl. Surf. Sci., 2016, 387, 539-545.
[13]
Zhang, W.J.; Pei, X.B.; Yang, B.; He, H.B. Effects of boron content and calcination temperature on properties of B-TiO2 photocatalyst prepared by solvothermal method. J. Adv. Oxid. Technol., 2014, 17, 66-72.
[14]
Simsek, E.B. Solvothermal synthesized boron doped TiO2 catalysts: Photocatalytic degradation of endocrine disrupting compounds and pharmaceuticals under visible light irradiation. Appl. Catal. B Environ, 2017, 200, 309-322.
[15]
Han, C.; Andersen, J.; Likodimos, V.; Falaras, P.; Linkugel, J.; Dionysiou, D.D. The effect of solvent in the sol–gel synthesis of visible light-activated, sulfur-doped TiO2 nanostructured porous films for water treatment. Catal. Today, 2014, 224, 132-139.
[16]
Derikvandi, H.; Nezamzadeh-Ejhieh, A. Increased photocatalytic activity of NiO and ZnO in photodegradation of a model drug aqueous solution: Effect of coupling, supporting, particles size and calcination temperature. J. Hazard. Mater., 2017, 321, 629-638.
[17]
Bahrami, M.; Nezamzadeh-Ejhieh, A. Effect of supporting and hybridizing of FeO and ZnO semiconductors onto an Iranian clinoptilolite nano-particles and the effect of ZnO/FeO ratio in the solar photodegradation of fish ponds waste water. Mater. Sci. Semicond. Process., 2014, 27, 833-840.
[18]
Cao, B.; Li, G.; Li, H.X. Hollow spherical RuO2@TiO2@Pt bifunctional photocatalyst for coupled H2 production and pollutant degradation. Appl. Catal. B Environ, 2016, 194, 42-49.
[19]
Sun, G.H.; Zhu, C.S.; Zheng, J.T.; Jiang, B.; Yin, H.C.; Wang, H.; Qiu, S.; Yuan, J.J.; Wu, M.B.; Wu, W.T.; Xue, Q.Z. Preparation of spherical and dendritic CdS@TiO2 hollow double-shelled nanoparticles for photocatalysis. Mater. Lett., 2016, 166, 113-115.
[20]
Zhang, W.J.; Pei, X.B.; Bai, J.W.; He, H.B. Calcination conditions on the properties of porous TiO2 film. J. Mater. Eng. Perform., 2014, 23, 1049-1054.
[21]
Scherrer, P. Determination of the size and internal structure of colloid particles by X-ray. Nachr. Ges. Wiss. Goettingen, Math.-. Phys. Kl., 1918, 1918, 98-100.
[22]
Su, H.D.; Ma, Z.; Hu, T.T.; Zhang, W.J.; He, H.B. Sol-gel synthesis of χTiO2/HZSM-5 composite photocatalyst on degradation of Reactive Brilliant Red X3B. Curr. Nanosci., 2017, 13, 292-298.
[23]
Grzmil, B.; Gleń, M.; Kic, B.; Lubkowski, K. Preparation and characterization of single-modified TiO2 for pigmentary applications. Indus. Eng. Chem. Res., 2011, 50, 6535-6542.
[24]
Moon, S.C.; Mametsuka, H.; Suzuki, E.; Nakahara, Y. Characterization of titanium-boron binary oxides and their photocatalytic activity for stoichiometric decomposition of water. Catal. Today, 1998, 45, 79-84.
[25]
Derikvandi, H.; Nezamzadeh-Ejhieh, A. Synergistic effect of p-n heterojunction, supporting and zeolite nanoparticles in enhanced photocatalytic activity of NiO and SnO2. J. Colloid Interface Sci., 2017, 490, 314-327.
[26]
Shams-Ghahfarokhi, Z.; Nezamzadeh-Ejhieh, A. As-synthesized ZSM-5 zeolite as a suitable support for increasing the photoactivity of semiconductors in a typical photodegradation process. Mater. Sci. Semicond. Process., 2015, 39, 265-275.


Rights & PermissionsPrintExport Cite as

Article Details

VOLUME: 15
ISSUE: 3
Year: 2019
Page: [289 - 295]
Pages: 7
DOI: 10.2174/1573413714666180717112803
Price: $58

Article Metrics

PDF: 23
HTML: 4