Preparation of Substituted Compounds of Lithium Indium Bromide and Fabrication of All Solid-State Battery

Author(s): Yasumasa Tomita*, Hiroo Nishiyama, Koji Yamada, Yoshiumi Kohno, Kenkichiro Kobayashi.

Journal Name: Recent Innovations in Chemical Engineering

Volume 10 , Issue 1 , 2017

Graphical Abstract:


Abstract:

Background and Objective: Li3InBr6-yXy (X=F, I) was synthesized and the substitution effect on ionic conductivity was investigated.

Method: An all solid state secondary battery was fabricated using Li3InBr6-yXy (X=F, Cl, I) and evaluated. Li3InBr6-yFy was single phase at y ≤ 3. The lattice constants for both compounds were decreased with an amount of F. The conductivity of Li3InBr6-yFy was decreased with y and electrochemical stability was improved by the substitution. The conductivity in Li3InBr6-yIy(y ≤ 3) was changed with y and Li3InBr3I3 showed the highest value in these compounds to be 3 ×10-3 Scm-1 at 333 K. 7Li NMR spectra in Li3InBr6-yIy was sharp and it was confirmed the diffusion of Li ion was fast at room temperature. Batteries using Li3InBr5F could be stably charged and discharged for 10 cycles.

Results and Conclusion: The discharge capacity increased in the first few cycles and the maximum value of 81 mAhg-1 was obtained in the fourth cycle.

Keywords: Solid electrolyte, ionic conductivity, Li-ion secondary battery, all solid-state battery, substitution effect, phase transition.

Rights & PermissionsPrintExport

Article Details

VOLUME: 10
ISSUE: 1
Year: 2017
Page: [12 - 17]
Pages: 6
DOI: 10.2174/2405520410666170614114423
Price: $58

Article Metrics

PDF: 9
HTML: 1
EPUB: 1
PRC: 0